Manufacturers and Exporters of High Quality Brazing and Welding Alloys that include
Silver Brazing Alloys (Cadmium Bearing, Cadmium Free and for Tungsten Carbide Tipped
Tools), Copper Based Brazing Alloys (Brass, Silicon Bronzes and Nickel Bronzes),
Silver Copper Phosphorus Brazing Alloys, Aluminium Filler Wires and their Fluxes.
Fluxes
We manufacture a wide range of fluxes, which can be put to varied uses. Fluxes consist of mild organic acid or strong inorganic acid which promotes high speed cleaning of metals with strong surface oxides and are generally used for silver brazing, phosphorus/copper brazing, solder and aluminum.
Product |
Product Description |
Product Cost |

ALFA ALUMFLUX |
It is used for brazing aluminium alloys and its alloys. Equivalent to ESAB ALOTECTIC Flux |
|
|

ALFA BRAZOFLUX |
It is used for brazing or fusion welding of various ferrous and non ferrous metals and alloys like cast iron, steel , brass etc. using Cu-Zn (Brass) filler metals. Equivalent to ESAB BRAZOTECTIC Flux. |
|
|

ALFA BRONZOFLUX |
It is used for brazing various ferrous and non-ferrous metals and alloys using Cu-Sn (Bronze) based filler metals. Equivalent to ESAB BRONZOTECTIC Flux |
|
|

ALFA CASTOFLUX |
It is used for welding Cast Iron. Equivalent to ESAB CASTOX Flux. |
|
|

ALFA SILFLUX |
It is an all purpose, low temperature flux for use in brazing ferrous and non ferrous metals and alloys using silver brazing filler metals. It begins to melt and dissolver oxides at 340`C and becomes fully molten at about 600`C and provides adequate protection upto 750`C. Excellent in hot rodding operation used to braze weld where the hot brazing rod is plunged into the dry powder. It can be easily cleaned using hot water. Equivalent to ESAB RUPATAM A Flux |
|
|

ALFA SILFLUX-A |
Recommended for use in 650`C-815`C. Excellent in hot rodding operations. For applications where a dry volatile flux is required. It can be easily cleaned up. Equivalent to HANDY DRY Flux 6040. |
|
|

ALFA SILFLUX-B |
The temperature range of this flux is 600`C-925`C. It is recommended for brazing tungsten and chromium carbides, molybdenum alloys and high chromium stainless steels. It is useful where local overheating may occur, as in fast induction heating. It is available in powder and paste form. Equivalent to HANDY Flux type B-1 |
|
|

ALFA SILPASTE |
It is general purpose, low temperature flux in paste form which provides creamy smooth consistency and excellent adhesion. It begins to melt and dissolve oxides at 320`C, is fully molten at 600`C and it provides full protection upto 870`C. It is used for brazing all ferrous metals and non-ferrous alloys. It can be easily cleaned up in hot water. Equivalent to HANDY PASTE Flux. |
|
|